Product Description:

Water-based epoxy, two-component system.
Characterised by great hardness, high bond strength, and compressive and flexural strengths in the cured state.
Resistant to a multitude of acids, alkaline solutions, concrete-damaging water, cleaning agents, seawater and brine.
Easily washed off with water when fresh.
Protected against bacterial attack and fungal infestation.
Very smooth, ease of processing.
Very low emission.

Areas of Application:

ASODUR®- EPG is used:

For bonding ceramic tiles and boards using the thin-bed method, on concrete, screed, plaster, old, tiled finishes and other substrates.
For grouting ceramic tile and board coverings
In interior and exterior areas
For heated substrates
For levelling minor unevenness on concrete, screed and plaster surfaces
ASODUR®-EPG is used in canteen kitchens, laboratories, swimming pools, dairies, meat processing plants and other areas of the food and chemical industry.

Application:

Both A (resin) and B (hardener) components are delivered in the predetermined mix ratio. Comp. B
is added completely to comp. A. The two components are mixed with a mechanical agitator at max. 300 min-1. (Slow-running drill with a whisk). Mix very thoroughly! It is imperative to also stir thoroughly from the sides and bottom so that the hardener is evenly distributed! Continue stirring until the mixture becomes homogenous. Do not apply from the delivered packaging. Transfer the mixed material into a separate, clean container and stir again.

Coatings:

Abrasive strain during use may cause scratches in the joint surface, which will be visible, particularly in the case of dark colours. This will not have a negative impact on functional capability.

At low temperatures, it is recommended to heat the material in a water bath at approx. +50 °C before use and then let it cool down to room temperature. This restores the processing properties.
Low object temperatures increase consumption. The material thus loses its good workability, and the reaction times are prolonged.
High temperatures shorten the processing time.
The colour shades may exhibit slight differences.
in colour due to raw material fluctuations. Therefore, contiguous surface sections should be coated using the same production batch.